Product |
General Characteristics |
Base Materials |
Technical Data |
LPP1 |
Primarily intended for mechanical applications where electrical properties are of secondary importance. Not recommended for high humidity applications
Alternative to: Attwater - B4, Bakelite Hylam - P101 |
Paper, Phenolic, Resin |
 |
LPP2 |
Suitable for general electrical insulating requirements. Good machineability |
Paper, Phenolic, Resin |
 |
LPP3 |
Excellent electrical insulating properties in high humidity applications. Has minimum cold flow characteristics. |
Paper, Phenolic, Resin |
 |
LPF1 |
Made from fine weave cotton cloth. Suitable for electrical application requiring good moisture resistance, machining properties |
Cotton cloth, Phenolic Resin |
 |
LPF2 |
Made from medium weave cotton cloth. Suitable for machining and mechanical application and as high density and good moisture resistance |
Cotton cloth, Phenolic Resin |
 |
LPF3 |
Made from cotton fabric weighing over four ounces per square yard. Has high impact strength and resiliency. Not recommended for electrical application. |
Cotton cloth, Phenolic Resin |
 |
LPF4 |
Same cotton fabric as grade LPF2. Suitable for application requiring good moisture resistance, high impact strength and good electrical properties |
Cotton cloth, Phenolic Resin |
 |
LPFG |
Made from fine weave cotton cloth, special resin with graphite inclusion. Not recommended for electrical application |
Cotton cloth, Phenolic Resin |
 |
SR2B |
Good wear, well bonded, dimensionally stable under operating conditions. Specially conditioned during fabrication to further protect. |
Cotton cloth, Phenolic Resin |
 |
ARC2 |
A high temperature material to replace materials containing Asbestos. Low moisture absorption. Excellent wear. |
Cotton, Special Phenolic Resin |
 |
LNP342 |
Heat stabilised, engineered not to shrink. With excellent impact and bond strength. With low creep. |
Cotton, Phenolic Resin |
 |
LEL635 |
Low water absorption good dimensional stability and excellent chemical resistance. |
Cotton, Epoxy Resin |
 |
ARK2 |
Designed to have good wear characteristics, low shrinkage and long term creep resistance. A high temperature material. |
Kelvar, Phenolic Resin |
 |
LNP193P |
Excellent mechanical strength at elevated temperatures. |
Kevlar, Phenolic Resin |
 |
ARG |
Good mechanical strength with high heat resistance. Good dimensional stability. Good moisture resistance |
Glass, Phenolic Resin |
 |
LG7 |
Excellent Anti - Tracking and Arc Resistance. Low water absorption |
Glass, Silicon Resin |
 |
LEO |
It has good electrical properties and high strength which are maintained at high temperatures. Flame retardant suitable for mechanical, electric and electrical applications |
Woven Glass, Epoxy |
 |
LM36 |
Excellent dielectric and mechanical properties at higher temperatures. |
Glass Epoxy, Resin |
 |
GPO3/LGP |
Formulated for superior electrical, thermal and mechanical properties Glastic UTR 1494 is the industry standard for flame and arc/track resistant electrical insulation. |
Glass, Polyester Resin |
 |
SG200 |
A high strength and high temperature laminate with high performance features. |
Glass, Polyester Resin |
 |
FHT |
Highly flexible, excellent dieletric strength with high heat resistance |
Glass, Polyester Resin |
 |
LM5 |
High mechanical strength, flame retardant, good heat and arc resistant properties. |
Glass, Melamine Resin |
 |
LSAT |
A high strength - high temperature laminate with excellent mechanical, thermal and electrical properties. |
Mica Silicon, Resin |
 |
LSLP |
Flexible and thermally resistant. Mainly used as slip plane insulation. |
Mica, Silicon Resin |
 |
SINDANYO H91 |
Non-asbestos, chemically inert and non-combustible fibre reinforced cement boards. |
Fibre Cement Board |
 |